Shin Yo Chemical Co.,Ltd

Fire Cote X210c(CP) STRUCTURAL STEEL INTUMESCENT
FIRE-RESISTANT COATING COMPOUND



1. PRODUCT DESCRIPTION

Fire Cote X210c(CP) is a highly flexible intumescent type fire resistant coating.

Fire Cote X210c(CP) is suitable for application on iron, steel, structural steel, and other surfaces where maximum fire protection coupled with a highly flexible, abrasion resistant, smooth finish is desired. When attacked by fire and/ or high heat, the coating puffs up
(intumesce) and forms a thick, dense fire barrier, thus affording maximum burn through(fire) protection.

This foam layer retards the penetration of heat to the substrate thus insulation the surface.


2. SURFACE PREPARATION

Surface preparation should be carried out according to good painting practices.

All dirt, grease, oil, wax, rust, and other foreign matter must be removed.

NEW SURFACES:

New metal surfaces must be primed. Apply Metal primer or two Component Epoxy Primer. After drying, apply Fire Cote X210c(CP).

PREVIOUSLY PAINTED SURFACES:

Fire Cote X210c(CP) may be applied directly to most existing paints that are tightly adherent, and in good condition.

However, we recommend spot testing for lifting.

If lifting occurs, consult with SHIN YO Fire Cote Corp.



3. APPLICATION

It can be applied by brush, roller or
conventional heavy duty

spray equipment. Stir thoroughly and apply, using a full bodied coat.



4. THEORETICAL COVERAGE

1. 0.236m2/Liter



5. DRYING TIME

The coating should be allowed to dry and cure for 72 hours if possible, but no less than 24 hours, prior to topcoating.



6. MIXING PROCEDURE

Due to possibld setting of contents during shipping and storage, the Product should be throughly mixed from bottom to top of the container.



7. PRODUCT SPECIFICATION

Specific gravity : 1.30  ? 0.2
Solids : 72  ?4%
Viscosity : 5,000 cps UP



8. COLOR

white.

9. PACKING

18 liter container